SIGMA OIL FILLER

Lime free filler, surface leveler based on acrylic copolymer
waterbased resins developed for filling/smoothing of internal cement
based building materials and boards
PRINCIPAL CHARACTERISTICS
– for interior use
– good filling smoothing and leveling properties
– unsaponifiable
– smooth surface produced
– easy to abrade
– good adhesion to primed substrates
– good cohesive strength
– emulsion finishes may be applied direct
– may be applied up to 1mm per coat
– multiple coats may be applied
– conforms to environmental specifications
COLOUR AND GLOSS
off-white – flat

Product Details
SKU: 916 Category: Tags: ,

Basic Data At 20 °c

Mass density
approx. 1.79g/cm³
Solids content
approx. 72% ± 2% by volume
Recommended dry film
200μm – 1mm
Theoretical
approx. 0.5 m2 /ltr at 1mm
spreading rate
depending on the nature and condition of the substrate and the
application method employed
Touch dry after
approx. 2 hours
Overcoating interval
min. 12 hours
max. no limitations
Shelf life (cool, dry place)
12 months

New primed substrates:
– dry and free from mortar splashes
– all surface contamination and dust must be removed
– cracks should be raked out before filling
previously painted (maintenance)

– remove all contamination, loose and flaking paint from the surface
– when used for patching work, spot prime all bare areas
– cracks should be raked out and primed before filling.

Recommended Primer
– 0805 Sigma Masonry Primer
– 0852 Sigma Acrylic Primer Sealer
Recommended finish types
– Sigma smooth waterborne type finishes

Method Of Application

Tools:
stainless steel filling knife, trowel or Swedish knife

Recommended thinner:
sweet water

Volume of thinner:
max. 3%

Environmental

Complies with VOC specifications such as LEED etc.

Reviews

There are no reviews yet.

Be the first to review “SIGMA OIL FILLER”

Your email address will not be published. Required fields are marked *

About SIGMA OIL FILLER


Quality interior filler coat with a specific oil, for concrete, cement based building and boards.


  • Good cohesive strength

  • Smooth surface produced

  • Multiple coats may be applied

  • Excellent sealing properties

  • Resistant to alkali

  • Provides stability to friable and powdery substrates