SIGMA SOLACRYL SEMI GLOSS

Adhesive based on a modified polyvinyl acetate copolymer developed
to give optimal adhesion between Sigmascan and the substrate
PRINCIPAL CHARACTERISTICS
– for interior use
– very good adhesion
– flexible
– almost odourless
– easy to apply
– developed for use with Sigmascan
COLOUR AND GLOSS
milky-white

Product Details
SKU: 883 Category: Tags: ,

Basic Data At 20 °c

Mass density
approx. 1.05g/cm3
Solids content
approx. 38% by volume
Recommended dry film
25 – 30μm
Theoretical
approx. 15.2 m2/ltr @ 25 μm
approx. 12.6 m2/ltr @ 30 μm
spreading rate
depending on the nature and condition of the substrate and the
application method employed
Touch dry after
approx. 3 hours
Overcoating interval
min. 8 hours
max. no limitation
Shelf life (cool, dry place)
12 months
Flashpoint
39 °C

New primed substrates
– dry and clean primed concrete, cement render and plaster type
– dry and clean primed timber
– dirt, dust and other surface contamination must be removed
previously painted substrates
– free from defective or poorly adhering paint films
– wash intact or remaining paint films with a 3% ammonia solution
– not recommended directly over unstable coatings

Recommended primer
– 0804 Sigmafix Primer
– 0852 Sigma Acrylic Primer Sealer
Recommended filler
– 0896 Sigma Concrete Filler (internal and external)
Recommended finish
– applied in two coats by spray @ 25-30μm dft per coat

Method Of Application

AIRLESS SPRAY
Recommended thinner
21-22 (flashpoint 50 °C)
Volume of thinner
0 – 5%
AIR SPRAY
Recommended thinner
21-22 (flashpoint 50 °C)
Volume of thinner
5 – 10%
BRUSH AND ROLLER
Recommended thinner
21-22 (flashpoint 50 °C)
Volume of thinner
0 – 5%
CLEANING SOLVENT
21-22 (flashpoint 50 °C)

Environmental

Complies with VOC specifications such as LEED etc.

Reviews

There are no reviews yet.

Be the first to review “SIGMA SOLACRYL SEMI GLOSS”

Your email address will not be published. Required fields are marked *

About SIGMA SOLACRYL SEMI GLOSS


High quality, non yellowing solvent based acrylic semi gloss finish.


  • Very good colour and gloss retention properties

  • Anti-carbonation properties

  • High UV resistance