SIGMARITE WL FILLER

Two component polyamide cured epoxy surface filler
PRINCIPAL CHARACTERISTICS
– good adhesion to steel, cement based building materials and
various plastics and wood
– ideal for use as a skim coat for filling grain on wood and profile on concrete and render
– good water and chemical resistance
– can be overcoated with alkyd, chlorinated rubber, vinyl, epoxy and polyurethane coatings
COLOUR AND GLOSS
white – eggshell

Product Details
SKU: 897 Category: Tags: ,

Basic Data At 20 °c

( For mixed product )
Mass density
approx. 1.4g/cm3
Solids content
approx. 73% by weight
Recommended
dry film thickness
up to 2 mm
Theoretical
spreading rate
5.2 kg/m2 for 2 mm
Touch dry after
approx. 1 hour
Overcoating interval
min. 16 hours*
max. 10 days*
Full cure after
7 days*
Shelf life (cool,dry place)
12 months
Flashpoint
base 17 °C – hardener 26 °C

– Substrate must be dry and free from any contamination
– if substrate shows high absorption it is advisable to prime with 7406 Sigmacover 211
– substrate temperature must be above 5 °C and at least 3 °C
above the dew point

Method Of Application

– Mixing ratio: by weight; base to hardener 83.5 : 16.5
– the temperature of the mixed base and hardener should be above
15 °C, otherwise extra solvent may be required to obtain the
correct application viscosity
Induction time at 20 °C
none
Potlife at 20 °C
4 hours*
APPLICATION TOOLS
– stainless steel filling knife, trowel or Swedish knife
– if necessary to smooth the surface of filler use thinner 91-92
(flashpoint 20 °C)
CLEANING SOLVENT
90-53 (flashpoint 30 °C)

Environmental

Complies with VOC specifications such as LEED etc.

Reviews

There are no reviews yet.

Be the first to review “SIGMARITE WL FILLER”

Your email address will not be published. Required fields are marked *

About SIGMARITE WL FILLER


Two component polyamide cured epoxy surface filler


  • Good adhesion to steel, cement based building materials and
    various plastics and wood